2630 d 1 mm 1000 g

containing lead

• halide-activated resin fluxes
• high activity, good spread and high residue reliability
• optimal wetting and spreading properties
• shiny solder joints with minimal flux residues
• flux residues - can be left on the PCB
• woldering operations on transformers and soldering copper cables with large cross sections
• when a stronger flux is needed due to the high termal capacity of the components that require soldering



• hand and robot soldering
• electrotechnology
• melting range: 183...190°C
• flux type (IEC 61190-1-3 ROM1): 1.1.2.B
• flux content: 2.2%
• corrosive effects (DIN 8516): none
• alloy (ISO 9453:2006): S-Sn60Pb39Cu1
• flux core: 3 core

Stannol series 2630 View larger

2630 d 1 mm 1000 g

8312 2630 d 1 mm 1000 g 397233 397233 containing lead. • halide-activated resin fluxes• high activity, good spread and high residue reliability• optimal wetting and spreading properties• shiny solder joints with minimal flux residues• flux residues - can be left on the PCB• woldering operations on transformers and soldering copper cables with large cross sections• when a stronger flux is needed due to the high termal capacity of the components that require soldering • hand and robot soldering• electrotechnology• melting range: 183...190°C• flux type (IEC 61190-1-3 ROM1): 1.1.2.B• flux content: 2.2%• corrosive effects (DIN 8516): none• alloy (ISO 9453:2006): S-Sn60Pb39Cu1• flux core: 3 core